HSS M2 Flat Bar

Name: HSS M2 Flat Bar
Brand: Swastik Metals
Price: 1400 INR
Availability: InStock

Price 1400 INR/ Kilometer

Get a Price/Quote

MOQ : 100 Kilograms

HSS M2 Flat Bar Specification

Corrosion Resistant
Moderate, can be improved with coating

Heat Resistance
Yes

Size
Customized as per requirement

Hardness
62-65 HRC (after heat treatment)

Material Composition %
W (5.50-6.75%), Mo (4.50-5.50%), Cr (3.75-4.50%), V (1.75-2.20%), C (0.85-0.95%), Fe (balance)

Recyclable
Yes

Diameter
Not applicable (flat bar)

Product Form
Flat Bar

Tensile Strength
Above 690 MPa

Coating Type
Uncoated or TiN/other coatings on request

Product Name
HSS M2 Flat Bar

Steel Type
High Speed Steel

Steel Product Type
Flat Bar

Thickness
3mm to 50mm

Shape
Rectangular/Flat

Steel Standard
ASTM, DIN, JIS, BS

Composition
Tungsten, Molybdenum, Chromium, Vanadium, Carbon, Iron

Application
Used for manufacturing cutting tools, dies, punches, and machine parts where high strength and durability are required.

Weight
Varies based on dimensions, typically calculated per meter

Material Grade
HSS M2

Finish Type
Bright/Polished/Black

Usage
Tool making, dies, cutters, wear components

Edge Condition
Mill Edge or Sheared Edge

Delivery Condition
Annealed or Hardened and Tempered

Minimum Order Quantity
As per supplier

Flatness Tolerance
Tight tolerances available upon request

Density
8.1 g/cm3

Machinability
Good, can be machined in annealed condition

Impact Strength
High

HSS M2 Flat Bar Trade Information

Minimum Order Quantity
100 Kilograms

Payment Terms
Cash Advance (CA), Cash in Advance (CID)

Supply Ability
2000 Kilograms Per Month

Delivery Time
10 Days

Main Domestic Market
All India

About HSS M2 Flat Bar

Our high-speed steel HSS M2 Flat Bar is a precision-crafted industrial steel product. Made from premium high-speed M2 steel, it is known for its high heat resistance, high wear resistance, and high cutting ability. This high-speed steel flat bar is designed for superior machining performance. It is suitable for high-end applications such as tooling, cutting and machining. It is specially heat-treated for optimal mechanical properties, ensuring reliability and accuracy in your processes. High-speed steel flat bars are commonly used in industries such as metalworking, aerospace and manufacturing, where high-quality cutting and machining instruments are essential for efficient and precise production. Reliance on our product to satisfy your industrial needs with perfection and accuracy.

Superior Strength and Durability

HSS M2 Flat Bars are valued for their excellent impact strength and remarkable wear resistance. After proper heat treatment, they exhibit a high hardness of 62-65 HRC, making them ideal for demanding tools and machine parts that endure rigorous use and require high operational reliability.

Precision Machinability and Flatness

These flat bars are specifically processed for good machinability, especially in the annealed state. Their flatness can be supplied to tight tolerances upon request, and edge conditions can be either mill or sheared-tailoring the product to exact application needs for toolmakers and manufacturers.

Versatile Applications in Toolmaking

Designed for use in high-performance environments, HSS M2 Flat Bars are widely applied in the manufacturing of cutting tools, dies, punches, and other machine components where toughness, thermal stability, and long operational life are essential. Their high heat and wear resistance ensure consistent performance.

FAQ's of HSS M2 Flat Bar:

Q: How is the machinability of HSS M2 Flat Bar ensured during manufacturing?

A: HSS M2 Flat Bar offers good machinability, especially when supplied in the annealed condition. The annealing process softens the material, making it easier to cut, shape, or machine as per tool and die requirements.

Q: What are the typical applications of HSS M2 Flat Bar?

A: This flat bar is widely used in the manufacture of cutting tools, dies, punches, and machine parts that need high strength, wear resistance, and the ability to retain hardness at high temperatures.

Q: When should I request hardened and tempered delivery condition?

A: You should opt for the hardened and tempered condition if you need the flat bar to exhibit its maximum hardness and strength immediately upon delivery. Otherwise, the annealed condition is preferred for easier machining before final heat treatment.

Q: Where is HSS M2 Flat Bar most commonly used?

A: HSS M2 Flat Bars are used in toolrooms, workshops, and manufacturing facilities involved in producing industrial cutting tools, dies, punches, and wear-resistant machine parts.

Q: What process is followed to achieve tight flatness tolerances?

A: Tight flatness tolerances are achieved through controlled rolling and heat treatment processes. If tighter than standard tolerances are needed, these can be specified at the time of order so the manufacturing process can be adjusted accordingly.

Q: How does the material composition of HSS M2 Flat Bar benefit its performance?

A: The combination of tungsten, molybdenum, chromium, vanadium, and carbon in precise percentages gives the bar high hardness, excellent heat resistance (up to 560C), and superior durability, making it ideal for high-wear tool applications.

Tell us about your requirement