16MNCR5 Case Hardening Steel Round Bar

Name: 16MNCR5 Case Hardening Steel Round Bar
Brand: Swastik Metals
Price: 92 INR
Availability: InStock

Price 92 INR/ Kilograms

Get a Price/Quote

MOQ : 100 Kilograms

16MNCR5 Case Hardening Steel Round Bar Specification

Size
Customizable; standard sizes 16mm - 100mm diameter

Tensile Strength
800-1000 MPa (after hardening and tempering)

Heat Resistance
Yes

Recyclable
Yes

Hardness
Core Hardness: 28-32 HRC; Case Hardness: up to 60 HRC (after carburizing)

Diameter
16mm to 100mm or as per requirement

Corrosion Resistant
Moderate; not stainless

Coating Type
Usually uncoated; can be oiled for rust prevention

Material Composition %
C: 0.14-0.19; Mn: 1.00-1.30; Cr: 0.80-1.10; S: 0.035; P: 0.035

Product Form
Solid round bar

Product Name
16MNCR5 Case Hardening Steel Round Bar

Steel Type
Alloy Steel

Steel Product Type
Round Bar

Thickness
Round bar; thickness interpreted as diameter, available from 16mm to 100mm or as specified.

Shape
Round

Steel Standard
DIN EN 10084 / BS 970 / AISI Equivalent 5115

Composition
C: 0.14-0.19%, Mn: 1.00-1.30%, Cr: 0.80-1.10%, S: 0.035%, P: 0.035%

Application
Used for case hardening applications in automotive, engineering components, gears, and shafts.

Weight
Varies according to dimension and length; calculated based on diameter and length.

Material Grade
16MnCr5

Finish Type
Bright, Peeled, Turned, or Black

Usage
Engineering, automotive gears, shafts, and wear-resistant parts

Delivery Condition
Annealed or as rolled

Minimum Order Quantity
As per supplier's policy

Machinability
Good in annealed condition

Non-magnetic
No, magnetic

Weldability
Fair; preheating recommended

Carburizing Temperature
880-950C

Impact Strength
High toughness after heat treatment

Maximum Bar Length
Up to 6000mm or as specified

16MNCR5 Case Hardening Steel Round Bar Trade Information

Minimum Order Quantity
100 Kilograms

Payment Terms
Cash Advance (CA), Cash in Advance (CID)

Supply Ability
2000 Kilograms Per Month

Delivery Time
100 Days

Main Domestic Market
All India

About 16MNCR5 Case Hardening Steel Round Bar

Explore the superior strength of the 16MNCR5 Case Hardening Steel Round Bar, meticulously decorated for first-class performance. This lofty, alloy steel bar is ideal for automotive, engineering components, gears, and shafts-delivering high impact toughness after heat treatment. Enjoy good machinability in the annealed state and fair weldability with preheating. Offered in a variety of surface finishes and customizable diameters (16mm-100mm), each bar conforms to recognized standards. Promotion underway-add to cart for efficient case-hardening solutions with lengths up to 6000mm.

Exceptional Features & Versatile Applications

The 16MNCR5 Case Hardening Steel Round Bar features a solid, polished surface finish, available bright, peeled, turned, or black. Used by manufacturers of automotive gears, engineering shafts, and wear-resistant parts, it ensures remarkable toughness once heat-treated. Its application surface suits areas requiring both core strength and a hardened outer layer, making it a preferred choice in high-demand settings. Bars are customizable, catering to unique dimensions or specialized engineering needs.

Global Reach, Prudent Packaging & Swift Dispatch

With main export markets in Asia, Africa, the Middle East, and Europe, the 16MNCR5 steel round bar is dispatched from leading FOB ports across India. Packaging is robust to preserve surface quality and prevent corrosion, typically using secure bundles and protective oiling. Outlay considerations are facilitated with competitive pricing. Each order is carefully dispatched, ensuring prompt delivery and minimal lead times so that production lines remain efficient and uninterrupted.

FAQ's of 16MNCR5 Case Hardening Steel Round Bar:

Q: How is the 16MNCR5 Case Hardening Steel Round Bar processed for optimal performance?

A: The bar is typically supplied annealed or as rolled, providing good machinability. For case hardening, it undergoes carburizing at 880-950C, followed by quenching and tempering, resulting in a hard, wear-resistant surface and a tough core.

Q: What applications benefit most from using this steel round bar?

A: It is ideal for case hardened components in automotive and engineering sectors, including gears, shafts, and other high-wear parts that demand both surface durability and internal toughness.

Q: When is preheating recommended during welding of this round bar?

A: Preheating is advised before welding due to the steel's composition (notably its chromium and manganese content) to prevent cracking and ensure sound weld integrity.

Q: Where can these bars be sourced or exported from?

A: They are readily available from reputable suppliers and traders in India, with exports dispatched globally, especially to Asia, Africa, and Europe, from major Indian ports.

Q: What is the benefit of using a customizable bar diameter and length?

A: Customizable sizes allow precise matching to your project requirements, minimizing material wastage, optimizing mechanical performance, and simplifying post-processing or assembly.